oloa

masterbatch suia mo le maualuga polyethylene bellows ma lapoa lapoa,
HDPE mo lalo, HDPE mo paipa curragated,

O lenei oloa e gaosia i le fa'aaogaina o tekinolosi fa'agasologa o le UNIPOL™.E fa'amoemoe mo le fa'aogaina i totonu o paipa e mana'omia ai le malosi o le hydrostatic umi ma le tete'e e fa'agesegese le tuputupu a'e.O fa'aoga talafeagai e aofia ai paipa fa'asoa kesi fa'alenatura, paipa fa'apisinisi tetele, eli, otaota, ma laina tautua vai a le malo.Fa'ata'ita'iga Tulaga Fa'apitoa: ASTM D 3350: fa'avasegaga o sela - Fa'alenatura - PE345464A - Uuliuli - PE345464C (Va'ai FA'AMATALAGA A) Inisetiute Pipe Palasitika (PPI): TR-4 - Pipe Faanatura - DGDB-2480 NT 3408 - ASTM PE3608 paipa vasega HDB - 1600psi @ 73 ° F - Paipa Uliuli - DGDB-2480 BK 3408 (Va'ai FA'AMATALAGA B) - ASTM PE3608 paipa vasega - 1600psi HDB @ 73 ° F ma 800psi HDB @ 140 ° F National Sanitation Foundation (NSF) Standard 14 ma 61 - Pipa Faanatura – DGDB-2480 NT 3608 – Paipa Uliuli – DGDB-2480 BK 3608 (Va’ai FAATUATUA B) Fa’atalanoa tulafono faatonutonu mo fa’amatalaga atoa.FA'AMATALAGA: (A) O numera muamua e lima o le fa'avasegaga o sela e fa'avae ile resini fa'anatura.O le numera mulimuli ma le mataitusi e fa'avae i luga o le resini uliuli (resin natura fa'atasi ma le 6.5% DFNF-0092).(B) O le resini faanatura e fa'aulu i lalo o tulaga talafeagai ma le carbon black masterbatch DFNF-0092 (6.5%).

Fa'aoga

1. Pipe talosaga
2.Natural kasa tufatufaina paipa
3. Large diameter paipa alamanuia
4. Laina
5. Lafoa'i
6. Laina tautua vai a le Malo

HDPEpa, ua taʻua o le PE curragted paipa, o se ituaiga fou o le paipa malamalama faia i le maualuga density polyethylene.It ei ai uiga o le mamafa mama, mamafa maualuga tetee, faigata lelei, fausiaina vave ma le ola umi.

O le lautele o le HDPE lua puipui puipui na gaosia i Saina o le φ400 ~ φ1400mm, lea e le gata ina manaʻomia ai le maualuga o le suavai o mea e faʻamalieina ai manaʻoga o meafaigaluega, ae faʻamalieina foi manaʻoga o le mama stiffness grade o oloa (S2 vasega e sili atu nai lo 8KN. /m2, mo se mea faapitoa, o le tele o le lautele, o le maualalo o le mama stiffness tau.. O lea e aumaia ai se faigata faapitoa i le filifilia o mea.. A maeʻa le tele o suʻega, e mafai e le Qilu HDPE2480 ona ausia ona manaʻoga gaosiga, ae o le mama mama o e le mafai e le oloa ona oʻo atu i le 8KN / m2. O le tau o le suʻega faʻamalosi mama i le vevela masani (23 ± 2 ℃) o le 6.2kN / m2, lea e manaʻomia ai le fesuiaiga o mea ma manaʻomia e aunoa ma le faʻaitiitia o le faʻatinoga o le uluai HDPE2480. O lona uiga, i lalo o le tulaga o le mautinoa o le mama fetuutuunai, maualalo le vevela aafiaga ma notch aafiaga malosi o le oloa; Faʻaleleia le faʻaogaina o mea e faʻaogaina e faʻamautinoa ai le tulaga o le faʻamalosi o oloa.
O le gaosiga o le gaosiga mo le maualuga o le faʻatumuina o le masterbatch o le tele o le polyethylene bellows e mafai ona fetaui ma manaʻoga o le tele o le faʻaogaina o le mama mama, le maualalo o le vevela, le malosi o le aʻafiaga ma le paʻu faʻapitoa.
Faʻafefiloi ma le 30-50% D50 = 2-7 ​​μm ultrafine calcium carbonate ma le 50-70% ultrafine talc paʻu, na saunia le paʻu tuʻufaʻatasia.
O le aofaʻi faʻatumu o mea faʻapitoa faʻapitoa e faia i mea faʻapipiʻi paʻu e mafai ona oʻo atu i le 50% ile HDPE tele-diameter bellows.I lalo o le tulaga o le HDPE∶ mea fou suia matai matai = 50∶50, o le mamafa o le paipa ma le caliber tutusa faateleina na o le 5 ~ 6%, ma lona modulus punou e oo atu i le 1360Mpa.O le tete'e ma le a'afiaga o le meafaitino ma le malosi fa'afefeteina o le 24Mpa e tutusa ma le mea muamua na fa'aleleia pe a fa'atumuina i le 30%: o le malosi fa'amalosi o le ≥24Mpa, ma le numera malepelepe o 10 fa'ata'ita'iga fa'atasi ai ma a'afiaga i le 0 ℃ e itiiti ifo i le 1, lea e faʻamalieina atoatoa manaʻoga o le tele-caliber HDPE bellows.
Fa'aaogā le 30 ~ 50% D50 = 2 ~ 7μm superfine calcium carbonate ma le 50 ~ 70% superfine talc pa'u e fa'afefiloi i totonu o le 100-vaega tu'ufa'atasi pa'u, fa'aopoopo le 0.2 ~ 1 vaega so'o fa'apipi'i i totonu o le pa'u tu'ufa'atasi ma fa'aoso mo le 5 ~ 10 minute ile 120 ~ 140 ℃.Ona faaopoopo lea o le 3 ~ 6 vaega o le suauu paʻepaʻe, 1 ~ 2 vaega o le stearic acid, 1 ~ 2 vaega o le suauʻu silicone hydroxyl ma le 20 ~ 30 vaega o le polyethylene poʻo le polypropylene faʻafefete tutusa pe a uma le mea, i le 150 ~ 190 ℃ vevela, e ala i le extruder sikuli masaga tutusa lona extrusion fefiloi ma granulating.
Ina ia mafai ona tuʻufaʻatasia le tele o le masterbatch ma faʻaitiitia le otaota ma le pefu i le gaosiga o le gaosiga, o le masterbatch e tipiina ma siaki e le ea e maua ai le tele o le vaega tutusa.
O le sui so'o fa'atasi o le titanate so'o so'o po'o aluminate so'o so'o po'o silane so'o so'o.